X.Y. Pang Z.Q. Liu S.Q. Wang J.K. Shang
材料科学技术（英）
Density functional theory was employed to investigate the bismuth segregation at Cu/Cu3Sn(010) interface. Five initial constructions were introduced by adopting the adhesion energy criterion. Among them, the so-called "between-Cu" construction in which the interface Cu atoms of Cu slab locate along Cu-Cu bond direction in Cu3Sn slab was found to be the most energy-favored at an adhesion energy of 1.96 J/m2. Based on this construction, five possible segregation sites were examined, and the most likely segregation site was determined with adhesion energy as low as 1.06 J/m2, which was almost half of the initial one. Comparing with other sites' adhesion energies, it was concluded that size effect took a large part in embrittlement. The analyses of atomic structure and electronic density revealed that the slabs shifted away from interfaces due to bismuth segregation, and the atoms around Bi atom were pressed away. This calculated work agreed qualitatively with reported experimental results.
关键词:
First-principles calculation
,
segregation
,
Bismuth
,
interface
,
SnBi solder.
赵宇
,
何忠治
,
翁宇庆
,
吴宝榕
金属学报
采用扫描Auger微探针(SAM)对微量Sn在高磁感取向硅钢中的晶界偏聚行为进行了研究,证明Sn在发生晶界偏聚时与取向硅钢中其它元素间没有明显的交互作用.在二次再结晶起始温度950℃,Sn在晶界仍有一定的偏聚量,作者认为,Sn通过在晶界偏聚起到了辅助抑制剂的作用.此外,根据理论分析,在高磁感取向硅钢中加入微量Sn可降低二次再结晶温度,这一结论与实验结果相吻合。
关键词:
高磁感取向硅钢
,
Sn
,
segregation
,
Auger
,
secondary recrystallization
潘晓林孙文儒杨树林李战郭守仁杨洪才胡壮麒
材料研究学报
铸态GH742合金中存在复杂的第二相组织和严重的枝晶偏析,Nb、Ti大量富集于枝晶间和MC碳化物、 Laves相、δ相、(γ+γ´)等析出相中.本文确定了γ基体的熔化温度为1160℃,并通过不同的均匀化处理确定了γ´相、(γ+γ´)共晶、MC碳化物、Laves相、δ相、Ni5Ce相及含氧硫稀土相等析出相的溶解温度.由于稀土相在1120℃发生熔化,提出一种GH742合金低温预处理加高温扩散的二次均匀化制度来扩大其均匀化温度区间,提高扩散退火温度, 从而获得均一的组织. 元素扩散计算结果表明,提高均匀化温度可以提高元素的扩散系数; Nb的偏析系数比Ti的小得多,达到完全均匀化需要很长的时间.
关键词:
金属材料
,
Ni-base superalloy
,
homogenization
,
microstructure transformation
,
segregation
,
diffusion
闵志先沈军冯周荣王灵水刘林傅恒志
金属学报
doi:10.3724/SP.J.1037.2010.00305
采用定向凝固技术结合液淬法对DZ125合金平界面和枝晶生长条件下溶质的偏析行为进行了研究, 通过EPMA定量测定γ基体中各元素的溶质含量和淬火平界面两侧固相和液相中的溶质含量, 分别获得了溶质再分配后固相中的溶质分布状态及溶质分配系数. 结果表明, 平界面生长条件下,液相中的熔体流动使溶质再分布始终处于非稳态. Al, Ti, Ta, Mo和Ni元素的溶质分配系数小于1; 而W, Cr和Co元素的溶质分配系数大于1, 溶质分布状态满足Scheil模型. 枝晶与平界面生长的溶质偏析行为基本一致, 然而,固相反扩散显著降低了枝晶生长过程中的溶质偏析.
关键词:
镍基高温合金
,
solute partition coefficient
,
segregation
,
directional solidification
骆良顺张宇民苏彦庆王新郭景杰傅恒志
金属学报
doi:10.3724/SP.J.1037.2010.00485
利用电阻加热和感应加热Bridgman定向凝固系统对非小平面包晶系模型合金Fe-Ni合金进行系统的定向凝固实验研究, 探索2种常规定向凝固条件下对流对包晶合金定向凝固过程中带状组织和宏观偏析的影响规律.发现在高G/V定向凝固过程中, 对流使包晶合金定向凝固过程中轴向和径向形成严重的宏观偏析, 从而使组织演化异常复杂且难以达到稳态.轴向宏观偏析体现在有限长试样从定向凝固开始至凝固结束都将发生初生相向包晶相的转变过程, 转变过程受合金成分和对流强度影响.径向宏观偏析体现在试样心部贫溶质易形成初生相, 边缘富集溶质易形成包晶相, 在径向上也存在初生相向包晶相的转变过程.
关键词:
包晶合金
,
directional solidification
,
convection
,
segregation
,
banding structure
曹虎
,
方必军
,
徐海清
,
罗豪甦
无机材料学报
研究了用改进的Bridgman法生长的PMNT62/38单晶在其生长过程中的分凝现象,研究了分凝导致的成分不均匀及其对介电和压电性能的影响.XRFA分析表明,PMNT62/38单晶底部的PbTiO3(PT)含量为x=35.2mol％,而顶部的PT含量为43mol％.底部晶体(001),(110)和(111)三种切型的晶片加电场极化后,其介电和压电性能出现了异常的现象.(110)切型的压电模量最大,为1200pC/N;(111)次之,为789pC/N;(001)最低,为371pC/N.极化后的(110)和(111)晶片在室温、1kHz频率下的相对介电常数(两种切型的εr都在10000左右),约为(001)晶片(εr-5000)的1倍,并且介电常数在低温端有上升的趋势.
关键词:
PMN-PT单晶
,
segregation
,
cut orientation
,
dielectric and piezoelectric properties
刘庆波
,
许少普
,
赵远
,
庞百鸣
钢铁研究
为解决生产的钢板出现较多探伤不合格的问题,采用高倍金相检验、扫描电镜及能谱分析等手段对探伤不合格的中厚板进行取样分析.发现探伤不合格的原因有:钢板的内部存在较严重的偏析,偏析带形成异常组织导致内部产生微裂纹;钢板夹杂物含量高,特别是硫化物夹杂严重影响钢板探伤质量;钢板存在较严重的疏松,在轧制过程中未完全焊合;钢板晶粒特别粗大,影响探伤检验结果;钢板虽然内部质量满足标准要求,但是由于表面氧化铁皮较厚,也会影响钢板探伤质量.通过优化精炼、连铸及轧制工艺后,钢板探伤三级合格率达到95.7％,探伤正品率达到了99.6％.
关键词:
探伤不合
,
偏析
,
异常组织
,
夹杂物
,
疏松
王雷
,
麻晗
,
李平
,
王晓娇
,
刘文庆
钢铁
研究了Si对高碳钢盘条珠光体相变及钢丝热稳定性的影响.研究表明,Si含量的增加可以明显地提高珠光体相变温度,且在高碳钢中增加相同含量的Si,不同相变温度下盘条硬度的增加值基本保持不变;三维原子探针分析结果表明,在高碳钢中添加一定量的Si可以减小盘条铁素体片层中C原子的偏聚程度,有利于提高C原子分布的均匀性;同时Si可以明显地提高渗碳体片层的球化温度,有利于钢丝热稳定性的提高.
关键词:
Si合金化
,
热稳定性
,
偏聚
,
珠光体相变